Au-free V/Al/Pt Contacts on n-Al0.85Ga0.15N:Si Surfaces of Far-UVC LEDs
H.K. Cho, I. Ostermay, T. Kolbe, J. Rass, and S. Einfeldt
Published in:
ECS J. Solid State Sci. Technol., vol. 13, no. 9, pp. 093009 (2024).
Abstract:
The feasibility of replacing the V/Al/Ni/Au contact on n-Al0.85Ga0.15N:Si commonly used in far-UVC LEDs with a Au-free V/Al/Pt contact has been investigated. It is shown that the V and Pt layer thicknesses play an important role for achieving a low contact resistivity and a smooth contact surface at a low annealing temperature. The specific contact resistivity of V(10 nm)/Al(120 nm)/Pt (40 nm) annealed at 700 °C for 5 min is comparable with that of V(15 nm)/Al(120 nm)/Ni(20 nm)/Au(30 nm) annealed at 850 °C for 30 s. Furthermore, the root mean square roughness of the optimized V/Al/Pt contacts was 8.3 nm as compared to 30 nm for V/Al/Ni/Au.
Ferdinand-Braun-Institut, Gustav-Kirchhoff-Str. 4, 12489 Berlin, Germany
© 2024 The Electrochemical Society (“ECS”). Published on behalf of ECS by IOP Publishing Limited. All rights, including for text and data mining, AI training, and similar technologies, are reserved.
Copyright Clearance Center
Full version in pdf-format.